搪瓷管的使用性能受温度影响

搪瓷管经过高温焙烧、冷却后，搪瓷管空气预热器采购，搪瓷与钢板就粘结在了一起。由于搪瓷的线膨胀系数和延伸率小于钢板的特性，冷却后搪玻璃的变形量会小于钢板的变形量，而搪瓷受到钢板的约束就会产生压应力。也就是说搪瓷管制成后，搪玻璃会存在一种预压缩应力，而钢板则存在预拉伸应力。

enamel tube through the high temperature roasting， cooling， enamel&steel plate is bonded together. because the characteristics of enamel of the coefficient of linear expansion&extension rate is less than the plate， deformation after cooling glass lining will be less than the amount of deformation of steel，&steel plate enamel ctrained will generate compressive stress. that is to say the enamel tube， glass lined there will be a pre compressive stress，&the steel plate are pre tensile stress.

由于预应力与线膨胀系数和延伸率相关，而线膨胀系数、延伸率又与温度密切相关，因此搪瓷管的工作温度对瓷管本身的使用会带来很大的影响。在这里需要注意温度的变化，如果温度变化大，很容易使搪瓷产生的应力超过使用应力，从而引起搪瓷的破坏，一旦搪瓷层遇到冷、热急变，极易发生爆瓷现象。

due to prestressing force&the coefficient of linear expansion&extension rate，&the coefficient of linear expansion， elongation&closely related with the temperature， so the enamel pipe working temperature on the porcelain tube itself use will have a great impact. here we need to pay attention to the change of temperature， if the temperature change is big，搪瓷管空气预热器， easy to cause the enamel of stress over the use of stress， so as to cause enamel damage， once the enamel layer encountered cold&hot blast， prone to burst phenomenon of porcelain.

关于空气预热器低温腐蚀的预防办法

　　空气预热器就是锅炉尾部烟道中的烟气通过内部的散热片将进入锅炉前的空气预热到一定温度的受热面。用于提高锅炉的热交换性能，降低能量消耗。所以我们就要做好低温腐蚀的预防，这是非常重要的事情，那么今天恒祥就来告诉大家预防和减轻低温腐蚀的主要措施：

　　1、少的量，这样不但点温度降低，而且减少了酸的凝结量，使腐蚀减轻；燃料脱硫，低氧燃烧，加入添加剂等方法。

　　2、高空气预热器冷端的壁温，搪瓷管空气预热器供应商，使其壁温高于烟气酸点温度，至少应高于腐蚀速度快时的壁温。实现后一途径的方法有热风再循环，加装暖风器等方法。

　　3、行中防止低温腐蚀的措施：

　　采用低氧燃烧。可以将烟气中so3大量降低，烟气下降，腐蚀速度减小，但是化学未完全燃烧有增加，但是排烟损失减少，锅炉效率稍有增加。

　　控制炉膛燃烧温度水平，减少so3的生成量。

　　定期吹灰，利于清除积灰，又利于防止低温腐蚀。

　　定期冲洗。如空预热器冷段积灰，可以用碱性水冲洗受热面清除积灰。冲洗后一般可以恢复至原先的排烟温度，而且腐蚀减轻。

　　避免和减少尾部受热面漏风。因漏风，受热面温度降低，腐蚀加速。---是空气预热器漏风，漏风处温度大量下降，导致---的低温腐蚀。